ネオジム焼結磁石
| ネオジム焼結磁石の物性 | ||||||||
| 学年 | 残留磁束 | Rev.Temp.-Coeff. Brの | 保磁力 | 固有保磁力 | Rev.Temp.-Coeff. HCJの | 最大。 エネルギー製品 | 最大。 動作温度 | 密度 |
| Br (KG) | HCB (あなた) | HCJ (あなた) | (BH) 最大 (MGOe) | g/cm3 | ||||
| N35 | 11.7-12.2 | -0.11～-0.12 | ≥10.9 | ≥12 | -0.58～-0.78 | 33-36 | 80℃ | 7.6 |
| N38 | 12.2-12.5 | -0.11～-0.12 | ≥11.3 | ≥12 | -0.58～-0.78 | 36-39 | 80℃ | 7.6 |
| N40 | 12.5-12.8 | -0.11～-0.12 | ≥11.5 | ≥12 | -0.58～-0.78 | 38-41 | 80℃ | 7.6 |
| N42 | 12.8-13.2 | -0.11～-0.12 | ≥11.5 | ≥12 | -0.58～-0.78 | 40-43 | 80℃ | 7.6 |
| N45 | 13.2～13.8 | -0.11～-0.12 | ≥11.6 | ≥12 | -0.58～-0.78 | 43-46 | 80℃ | 7.6 |
| N48 | 13.8-14.2 | -0.11～-0.12 | ≥11.6 | ≥12 | -0.58～-0.78 | 46-49 | 80℃ | 7.6 |
| N50 | 14.0～14.5 | -0.11～-0.12 | ≥10.0 | ≥12 | -0.58～-0.78 | 48-51 | 80℃ | 7.6 |
| N52 | 14.3-14.8 | -0.11～-0.12 | ≥10.0 | ≥12 | -0.58～-0.78 | 50-53 | 80℃ | 7.6 |
| N33M | 11.3-11.7 | -0.11～-0.12 | ≥10.5 | ≥14 | -0.58～-0.72 | 31-33 | 100℃ | 7.6 |
| N35M | 11.7-12.2 | -0.11～-0.12 | ≥10.9 | ≥14 | -0.58～-0.72 | 33-36 | 100℃ | 7.6 |
| N38M | 12.2-12.5 | -0.11～-0.12 | ≥11.3 | ≥14 | -0.58～-0.72 | 36-39 | 100℃ | 7.6 |
| N40M | 12.5-12.8 | -0.11～-0.12 | ≥11.6 | ≥14 | -0.58～-0.72 | 38-41 | 100℃ | 7.6 |
| N42M | 12.8-13.2 | -0.11～-0.12 | ≥12.0 | ≥14 | -0.58～-0.72 | 40-43 | 100℃ | 7.6 |
| N45M | 13.2～13.8 | -0.11～-0.12 | ≥12.5 | ≥14 | -0.58～-0.72 | 43-46 | 100℃ | 7.6 |
| N48M | 13.6-14.3 | -0.11～-0.12 | ≥12.9 | ≥14 | -0.58～-0.72 | 46-49 | 100℃ | 7.6 |
| N50M | 14.0～14.5 | -0.11～-0.12 | ≥13.0 | ≥14 | -0.58～-0.72 | 48-51 | 100℃ | 7.6 |
| N35H | 11.7-12.2 | -0.11～-0.12 | ≥10.9 | 17歳以上 | -0.58～-0.70 | 33-36 | 120℃ | 7.6 |
| N38H | 12.2-12.5 | -0.11～-0.12 | ≥11.3 | 17歳以上 | -0.58～-0.70 | 36-39 | 120℃ | 7.6 |
| N40H | 12.5-12.8 | -0.11～-0.12 | ≥11.6 | 17歳以上 | -0.58～-0.70 | 38-41 | 120℃ | 7.6 |
| N42H | 12.8-13.2 | -0.11～-0.12 | ≥12.0 | 17歳以上 | -0.58～-0.70 | 40-43 | 120℃ | 7.6 |
| N45H | 13.2-13.6 | -0.11～-0.12 | ≥12.1 | 17歳以上 | -0.58～-0.70 | 43-46 | 120℃ | 7.6 |
| N48H | 13.7-14.3 | -0.11～-0.12 | ≥12.5 | 17歳以上 | -0.58～-0.70 | 46-49 | 120℃ | 7.6 |
| N35SH | 11.7-12.2 | -0.11～-0.12 | ≥11.0 | 20以上 | -0.56～-0.70 | 33-36 | 150℃ | 7.6 |
| N38SH | 12.2-12.5 | -0.11～-0.12 | ≥11.4 | 20以上 | -0.56～-0.70 | 36-39 | 150℃ | 7.6 |
| N40SH | 12.5-12.8 | -0.11～-0.12 | ≥11.8 | 20以上 | -0.56～-0.70 | 38-41 | 150℃ | 7.6 |
| N42SH | 12.8-13.2 | -0.11～-0.12 | ≥12.4 | 20以上 | -0.56～-0.70 | 40-43 | 150℃ | 7.6 |
| N45SH | 13.2～13.8 | -0.11～-0.12 | ≥12.6 | 20以上 | -0.56～-0.70 | 43-46 | 150℃ | 7.6 |
| N28UH | 10.2～10.8 | -0.11～-0.12 | ≥9.6 | ≥25 | -0.52～-0.70 | 26-29 | 180℃ | 7.6 |
| N30UH | 10.8～11.3 | -0.11～-0.12 | ≥10.2 | ≥25 | -0.52～-0.70 | 28-31 | 180℃ | 7.6 |
| N33UH | 11.3-11.7 | -0.11～-0.12 | ≥10.7 | ≥25 | -0.52～-0.70 | 31-34 | 180℃ | 7.6 |
| N35UH | 11.8-12.2 | -0.11～-0.12 | ≥10.8 | ≥25 | -0.52～-0.70 | 33-36 | 180℃ | 7.6 |
| N38UH | 12.2-12.5 | -0.11～-0.12 | ≥11.0 | ≥25 | -0.52～-0.70 | 36-39 | 180℃ | 7.6 |
| N40UH | 12.5-12.8 | -0.11～-0.12 | ≥11.3 | ≥25 | -0.52～-0.70 | 38-41 | 180℃ | 7.6 |
| N28EH | 10.4～10.9 | -0.105～-0.120 | ≥9.8 | 30以上 | -0.48～-0.70 | 26-29 | 200℃ | 7.6 |
| N30EH | 10.8～11.3 | -0.105～-0.120 | ≥10.2 | 30以上 | -0.48～-0.70 | 28-31 | 200℃ | 7.6 |
| N33EH | 11.3-11.7 | -0.105～-0.120 | ≥10.5 | 30以上 | -0.48～-0.70 | 31-34 | 200℃ | 7.6 |
| N35EH | 11.7-12.2 | -0.105～-0.120 | ≥11.0 | 30以上 | -0.48～-0.70 | 33-36 | 200℃ | 7.6 |
| N38EH | 12.2-12.5 | -0.105～-0.120 | ≥11.3 | 30以上 | -0.48～-0.70 | 36-39 | 200℃ | 7.6 |
| N28AH | 10.4～10.9 | -0.105～-0.120 | ≥9.9 | ≥33 | -0.45～-0.70 | 26-29 | 230℃ | 7.6 |
| N30AH | 10.8～11.3 | -0.105～-0.120 | ≥10.3 | ≥33 | -0.45～-0.70 | 28-31 | 230℃ | 7.6 |
| N33AH | 11.3-11.7 | -0.105～-0.120 | ≥10.6 | ≥33 | -0.45～-0.70 | 31-34 | 230℃ | 7.6 |
| 注記： ・使用温度20℃±2℃で、上記の磁気パラメータと物理的特性をテストしましたが、必然的な磁力損失は5%以下です。・磁石の最高使用温度は、長さと直径の比率および環境要因により変化します。 。 | ||||||||
アドバンテージ：
これらの磁石の特性は従来のものよりもはるかに優れており、現在最も強力な用途に使用されています。 彼らのハイ
保磁力と高い残留磁気により、新しい設計が可能になり、スペースが限られている場所での適用磁場を増加できる可能性があります。
または強い磁場が必要な場所。
NdFeB 磁石は非常に腐食しやすいです。 したがって、表面保護コーティングが必要です。 NdFeB磁石の使用には条件があります
80℃から230℃までの幅広い温度範囲で測定可能です。 また、0℃以下の温度でも動作します。
応用：
ネオジム磁石は、エレクトロニクス、ブレーキ システム、
点滴、センサー、ローターやマイクロモーターの磁気システム、科学、医学分野（断層撮影、NMR分光計）など。
現在、NdFeB 磁石は世界中で大量に使用されています。 この材料の開発はまだ完了していません。 残留物
抗電界の強さは継続的に増加しています。 NdFeB 磁石の高エネルギーは、モーターやセンサーを構築できることを意味します
これはパフォーマンス効率の向上を意味します。 現在進行中の改善により、この興味深い素材を継続的に提供できるようになりました。
毎年新しい分野に導入されています。
記載されているすべての値は、IEC 60404-5 に従って標準サンプルを使用して決定されました。 以下の仕様は参考値であり、
異なる場合があります。 詳細については、当社のアプリケーション エンジニアにお問い合わせください。
ここにメッセージを書いて送信してください